HumiSeal 2A64 Description
HumiSeal 2A64 is a two component polyurethane conformal coating supplied as Parts A and B, suitable for general printed circuit board applications.
- HumiSeal 2A64 is characterized by high solids and low viscosity for ease of application and processing, and it fluoresces under UV light for inspection purposes.
- This coating is MIL-I-46058C qualified, and IPC-CC-830 and RoHS Directive 2011/65/EC compliant.
Technical data of HumiSeal 2A64
Property | Value |
---|---|
Density, per ASTM D1475 | 1.07 ± 0.03 g/cm³ |
Solids Content, % by weight | 55 ± 5 % per Fed-Std-141, Meth. 4044 |
Viscosity, per Fed-Std-141, Meth. 4287 | 130 ± 50 centipoise |
VOC | 501 grams/litre |
Recommended Coating Thickness | 25 - 75 microns |
Drying Time to Handle | 15 minutes per Fed-Std-141, Meth. 4061 |
Curing Condition to Reach Optimum Properties | 3 hrs @ 76°C |
Recommended Thinner | HumiSeal® Thinner 64 |
Recommended Stripper | HumiSeal® Stripper 1072 |
Pot Life at Room Temperature | 8 hours |
Shelf Life at Room Temperature, DOM | 12 months |
Thermal Shock | 50 cycles per MIL-I-46058C |
-65°C to 125°C | |
Coefficient of Thermal Expansion - TMA | 82 ppm/°C (Below Tg) |
255 ppm/°C (Above Tg) | |
Glass Transition Temperature - DSC | 12°C |
Modulus - DMA | 4101 MPa @ -40ºC |
2777 MPa @ 25ºC | |
2 MPa @ 80ºC | |
Flammability, per MIL-I-46058C | Self-Extinguishing |
Dielectric Withstand Voltage | >1500 volts per MIL-I-46058C |
Dielectric Breakdown Voltage | 3500 volts per ASTM D149 |
Dielectric Constant, at 1MHz and 25°C | 3.5 per ASTM D150-98 |
Dissipation Factor, at 1MHz and 25°C | 0.024 per ASTM D150-98 |
Insulation Resistance | 4.5 x 10^14 ohms (450TΩ) per MIL-I-46058C |
Moisture Insulation Resistance | 4.8 x 10^10 ohms (48GΩ) per MIL-I-46058C |
Fungus Resistance | Passes per ASTM G21 |
Application of HumiSeal 2A64
- Cleanliness of the substrate is of extreme importance for the successful application of the coating. Contamination under the coating could cause problems that may lead to assembly failures.
- For best performance, surfaces should be free of moisture, dirt, wax, grease, flux residues and all other contaminants.
- If this product will be applied over “no clean” assembly materials, the user should conduct adequate testing to verify compatibility and reliability of the coated assembly.
- Mixing ratio of Part A to Part B is 1:1 by volume. Prior to application, HumiSeal® 2A64 Parts A and B should be thoroughly mixed until a homogenous blend is achieved.
- Vigorous mixing is not recommended. The mixed coating should be allowed to settle for 30 minutes prior to use so that any air bubbles formed during blending can escape.
Brushing
- HumiSeal 2A64 may be applied by brush. Uniformity of the film depends on component density and operator's technique.
Dipping
- Depending on the complexity, density and configuration of components on the assembly, it may be necessary to reduce the viscosity of prepared HumiSeal 2A64 with HumiSeal Thinner 64 in order to obtain a uniform film.
- Once optimum viscosity is determined, a controlled rate of immersion and withdrawal (5-15 cm/min) will further ensure even deposition of the coating and ultimately a uniform film.
- During the application, evaporation of solvent causes an increase in viscosity that should be adjusted by adding small amounts of HumiSeal Thinner 64.
- Viscosity in the dip tank should be checked regularly, using a simple measuring device such as a Zahn or Ford viscosity cup.
Spraying
- HumiSeal 2A64 can be sprayed using conventional spraying equipment.
- Spraying should be done in an environment with adequate ventilation so that the vapour and mist are carried away the operator.
- The addition of HumiSeal Thinner 64 is necessary to ensure a uniform spray pattern resulting in pinhole-free film.
- The amount of thinner and spray pressure will depend on the specific type of spray equipment used and operator technique.
- The recommended ratio of prepared HumiSeal 2A64 to HumiSeal® Thinner 64 is 1:1 by volume; however the ratio may need to be adjusted to obtain a uniform coating.
Storage
- HumiSeal 2A64 Parts A and B should be stored away excessive heat or cold, in tightly closed containers.
- HumiSeal products may be stored at temperatures of 0 to 35°C.
- Prior to use, allow the product to equilibrate for 24 hours at a room temperature of 18 to 32°C.
Caution
- Application of HumiSeal Conformal Coatings should be carried out in accordance with local and National Health and Safety regulations.
- The solvents in HumiSeal Conformal Coatings are flammable.
- Material should not be used in presence of open flame or sparks.
- Use only in well-ventilated areas to avoid inhalation of vapours or spray. Avoid contact with skin and eyes.
Where to buy authentic HumiSeal 2A64 ?
Thanks to our strong reputation, Hicotech has earned the trust of numerous customers. Feel free to reach out to us for expert consultation and to avail the best pricing for the HumiSeal 2A64 product.
Contact information
Hotline/Zalo. 094 526 1931
Website. Hicotech.com.vn
Email: Sale@hicotech.com.vn
Xem thêm
Tin tức mới nhất
Có 0 đánh giá về HumiSeal 2A64